最小有效渗氮层深度、最低表面硬度与试验力之间的关系(JB/T 8555—1997) |
|||||||
最小有效渗 氮层深度 /mm |
最 低 表 面 硬 度 HV |
||||||
200~300 |
>300~400 |
>400~500 |
>500~600 |
>600~700 |
>700~800 |
>800 |
|
0.05 |
— |
— |
— |
HV0.5 |
HV0.5 |
HV0.5 |
HV0.5 |
0.07 |
— |
HV0.5 |
HV0.5 |
HV0.5 |
HV0.5 |
HV1 |
HV1 |
0.08 |
HV0.5 |
HV0.5 |
HV0.5 |
HV0.5 |
HV1 |
HV1 |
HV1 |
0.09 |
HV0.5 |
HV0.5 |
HV0.5 |
HV1 |
HV1 |
HV1 |
HV1 |
0.1 |
HV0.5 |
HV1 |
HV1 |
HV1 |
HV1 |
HV1 |
HV3 |
0.15 |
HV1 |
HV1 |
HV3 |
HV3 |
HV3 |
HV3 |
HV5 |
0.2 |
HV3 |
HV3 |
HV5 |
HV5 |
HV5 |
HV5 |
HV5 |
0.25 |
HV3 |
HV5 |
HV5 |
HV5 |
HV10 |
HV10 |
HV10 |
0.3 |
HV5 |
HV5 |
HV10 |
HV10 |
HV10 |
HV10 |
HV10 |
0.4 |
HV5 |
HV10 |
HV10 |
HV10 |
HV10 |
HV30 |
HV30 |
0.45 |
HV10 |
HV10 |
HV10 |
HV10 |
HV30 |
HV30 |
HV30 |
0.5 |
HV10 |
HV10 |
HV10 |
HV30 |
HV30 |
HV30 |
HV30 |
0.55 |
HV10 |
HV10 |
HV30 |
HV30 |
HV30 |
HV50 |
HV50 |
0.6 |
HV10 |
HV10 |
HV30 |
HV30 |
HV50 |
HV50 |
HV50 |
0.65 |
HV10 |
HV30 |
HV30 |
HV50 |
HV50 |
HV50 |
HV50 |
0.7 |
HV10 |
HV30 |
HV50 |
HV50 |
HV50 |
HV50 |
HV50 |
0.75 |
HV20 |
HV30 |
HV50 |
HV50 |
HV50 |
HV100 |
HV100 |
注:表内检验方法通常是指允许采用最大试验力,允许用较低的试验力代替表中规定的试验力,如用 HV10代替 HV30。 |